Select 410NiMo-AP

Stainless Steel / Flux Cored / Gas Shielded


Features

  • Modified to contain less chromium (Cr) and more nickel (Ni) to eliminate ferrite in the microstructure that improves mechanical properties.
  • Designed for welding in all positions. Well washed beads can be achieved when manipulating the puddle in both 100% CO₂ or 75-80% Ar/balance CO₂ shielding gas
  • Postweld heat treatment temperatures need to be closely monitored with this alloy type, as higher temperatures, i.e. 1150F, may result in rehardening due to untampered martensite in the microstructure after cooling to room temperature.
  • Application for this alloy is generally used to weld CA6NM castings or similar materials found in the power generation industry, especially with turbine blades and vanes.

Standard Diameters

in (mm)
  • 0.045 (1.2)
  • 1/16 (1.6)

Welding Positions

All Positions

Shielding Gas

  • 75-80% Ar + Balance CO₂
  • 100% CO₂
    Flow Rate: 40 – 50 CFM

Polarity

Direct Current Electrode Positive (DCEP)

Conformances

  • ASME SFA 5.22
    • E410NiMoT1-1
    • E410NiMoT1-4
  • AWS A5.22
    • E410NiMoT1-1
    • E410NiMoT1-4
  • TYPICAL WELD DEPOSIT CHEMISTRY (WT%)
    Shielding Gas C Cr Cu Mn Mo Ni P S Si
    100% CO₂ 0.02 11.80 0.03 0.31 0.50 4.55 0.011 0.006 0.36
    75% Ar/25% CO₂ 0.02 12.00 0.03 0.33 0.52 4.61 0.012 0.007 0.41
    Bismuth is not intentionally added and is not known to be at levels greater than 0.002 wt%

    Packaging (lbs (kg))

    33 (15) Spools, 60 (27.2) Coils, 500 (226.8) Round Drum, 800 (362.9) Hex Drum, 900 (408.2) Hex Drum